What are the factors that affect the performance of putty powder for internal and external walls? Today we will talk about this problem.

一、粉煤灰用量對內(nèi)外墻膩子粉性能的影響：隨著粉煤灰用量增加，膩子粘結(jié)強度逐漸降低;當(dāng)粉煤灰用量達(dá)30%以上時，強度降低相對較快。另外，隨著粉煤灰用量增大，膩子施工性能有所改善。綜合考慮，粉煤灰用量可控制在20%～30%范圍內(nèi)。

1、 The influence of fly ash content on the performance of putty powder for internal and external walls: with the increase of fly ash content, the adhesive strength of putty gradually decreases; when the amount of fly ash is more than 30%, the strength decreases relatively quickly. In addition, with the increase of fly ash dosage, the construction performance of putty is improved. Comprehensive consideration, the amount of fly ash can be controlled in the range of 20% - 30%.

二、水泥對內(nèi)外墻膩子粉的性能的影響：在水的作用下，水泥通過反應(yīng)形成交聯(lián)網(wǎng)狀結(jié)構(gòu)，因而能賦予膩子高粘結(jié)強度。當(dāng)水泥用量達(dá)15%后，再增加水泥用量，膩子粉的粘結(jié)強度增加較緩慢。同時，水泥用量過大，易引起膩子膜層甚至表面涂層起裂紋。因此水泥用量控制在10%～40%范圍較好。

2、 The effect of cement on the properties of putty powder for internal and external walls: under the action of water, the cement reacts to form a cross-linked network structure, which can endow the putty with high bond strength. When the amount of cement reaches 15%, the bond strength of putty powder increases slowly with the increase of cement content. At the same time, if the amount of cement is too large, it is easy to cause cracks in the putty film and even the surface coating. Therefore, it is better to control the cement dosage in the range of 10% - 40%.

三、乳膠粉對內(nèi)外墻膩子粉性能的影響：隨著乳膠粉用量的增加，膩子粘結(jié)強度逐步增大;乳膠粉用量在2.5%以下，膩子粘結(jié)強度隨乳膠粉用量增加較明顯;乳膠粉用量在2.5%以上，膩子粘結(jié)強度隨乳膠粉用量增加的幅度較小。由于隨著乳膠粉用量的增加，膩子的成本增大，并有導(dǎo)致施工性變差的可能，因而乳膠粉的用量在2.5%～3.5%范圍內(nèi)較佳。

3、 The influence of latex powder on the properties of putty powder for internal and external walls: with the increase of the amount of latex powder, the adhesive strength of putty increases gradually; when the amount of latex powder is less than 2.5%, the adhesive strength of putty increases obviously with the amount of latex powder; when the amount of latex powder is more than 2.5%, the increase range of putty bond strength with the amount of latex powder is small. Because the cost of putty increases with the increase of the amount of latex powder, and the construction performance may be worse, so the dosage of latex powder is better in the range of 2.5% - 3.5%.

另外，隨著乳膠粉用量增加，膩子膜層干擦洗質(zhì)量損失逐漸減少，當(dāng)乳膠粉用量達(dá)2.5%以上時，膩子膜層質(zhì)量損失趨于穩(wěn)定，且質(zhì)量損失很小。這主要是由于當(dāng)乳膠粉達(dá)到此用量時，乳膠粉分散成膠液后能很好地將顏填料與基材粘結(jié)起來。

In addition, with the increase of the amount of latex powder, the dry scrubbing mass loss of putty film gradually decreases. When the amount of latex powder is more than 2.5%, the quality loss of putty film tends to be stable and the quality loss is very small. This is mainly due to the fact that when the amount of latex powder reaches this level, the pigment and filler can be well bonded with the substrate after being dispersed into a glue solution.